A Langmuir–Blodgett (LB) film is a nanostructured system formed when Langmuir films - or Langmuir monolayers (LM)- are transferred from the liquid-gas interface to solid supports during the vertical passage of the support through the monolayers. LB films can contain one or more monolayers of an organic material, deposited from the surface of a liquid onto a solid by immersing (or emersing) the solid substrate into (or from) the liquid. A monolayer is adsorbed homogeneously with each immersion or emersion step, thus films with very accurate thickness can be formed. This thickness is accurate because the thickness of each monolayer is known and can therefore be added to find the total thickness of a Langmuir–Blodgett film.

The monolayers are assembled vertically and are usually composed either of amphiphilic molecules (see Chemical polarity) with a hydrophilic head and a hydrophobic tail (example: fatty acids) or nowadays commonly of nanoparticles.^[1]

Langmuir–Blodgett films are named after Irving Langmuir and Katharine B. Blodgett, who invented this technique while working in Research and Development for General Electric Co.

Historical background

Advances to the discovery of LB and LM films began with Benjamin Franklin in 1773 when he dropped about a teaspoon of oil onto a pond. Franklin noticed that the waves were calmed almost instantly and that the calming of the waves spread for about half an acre.^[2] What Franklin did not realize was that the oil had formed a monolayer on top of the pond surface. Over a century later, Lord Rayleigh quantified what Benjamin Franklin had seen. Knowing that the oil, oleic acid, had spread evenly over the water, Rayleigh calculated that the thickness of the film was 1.6 nm by knowing the volume of oil dropped and the area of coverage.

With the help of her kitchen sink, Agnes Pockels showed that area of films can be controlled with barriers. She added that surface tension varies with contamination of water. She used different oils to deduce that surface pressure would not change until area was confined to about 0.2 nm². This work was originally written as a letter to Lord Rayleigh who then helped Agnes Pockels become published in the journal, Nature, in 1891.Agnes Pockels’ work set the stage for Irving Langmuir who continued to work and confirmed Pockels’ results. Using Pockels’ idea, he developed the Langmuir (or Langmuir–Blodgett) trough. His observations indicated that chain length did not impact the affected area since the organic molecules were arranged vertically.

Langmuir’s breakthrough did not occur until he hired Katherine Blodgett as his assistant. Blodgett initially went to seek for a job at General Electric (GE) with Langmuir during her Christmas break of her senior year at Bryn Mawr College, where she received a BA in Physics. Langmuir advised to Blodgett that she should continue her education before working for him. She thereafter attended University of Chicago for her MA in Chemistry. Upon her completion of her Master's, Langmuir hired her as his assistant. However, breakthroughs in surface chemistry happened after she received her PhD degree in 1926 from Cambridge University.

While working for GE, Langmuir and Blodgett discovered that when a solid surface is inserted into an aqueous solution containing organic moieties, the organic molecules will deposit a monolayer homogeneously over the surface. This is the Langmuir–Blodgett film deposition process. Through this work in surface chemistry and with the help of Blodgett, Langmuir was awarded the Nobel Prize in 1932. In addition, Blodgett used Langmuir–Blodgett film to create 99% transparent anti-reflective glass by coating glass with fluorinated organic compounds, forming a simple anti-reflective coating.

Physical insight

Langmuir films are formed when amphiphilic (surfactants) molecules or nanoparticles are spread on the air at an air–water interface. Surfactants (or surface-acting agents) are molecules with hydrophobic 'tails' and hydrophilic 'heads'. When surfactant concentration is less than the minimum surface concentration of collapse and it is completely insoluble in water , the surfactant molecules arrange themselves as shown in Figure 1 below. This tendency can be explained by surface-energy considerations. Since the tails are hydrophobic, their exposure to air is favoured over that to water. Similarly, since the heads are hydrophilic, the head–water interaction is more favourable than air–water interaction. The overall effect is reduction in the surface energy (or equivalently, surface tension of water).

For very small concentrations, far from the surface density compatible with the collapse of the monolayer (which leads to polylayers structures) the surfactant molecules execute a random motion on the water–air interface. This motion can be thought to be similar to the motion of ideal-gas molecules enclosed in a container. The corresponding thermodynamic variables for the surfactant system are, surface pressure (

), surface area (A) and number of surfactant molecules (N). This system behaves similar to a gas in a container. The density of surfactant molecules as well as the surface pressure increases upon reducing the surface area A ('compression' of the 'gas'). Further compression of the surfactant molecules on the surface shows behavior similar to phase transitions. The ‘gas’ gets compressed into ‘liquid’ and ultimately into a perfectly closed packed array of the surfactant molecules on the surface corresponding to a ‘solid’ state. The liquid state is usually separated in the liquid-expanded and liquid-condensed states. All the Langmuir film states are classified according to the compressionality factor of the films, defined as -A(d (

)/dA), usually related to the in-plane elasticity of the monolayer.

The condensed Langmuir films (in surface pressures usually higher than 15 mN/m - typically 30 mN/m) can be subsequently transferred onto a solid substrate to create highly organized thin film coatings. Langmuir–Blodgett troughs

Besides LB film from surfactants depicted in Figure 1, similar monolayers can also be made from inorganic nanoparticles.^[3]

Pressure–area characteristics

Adding a monolayer to the surface reduces the surface tension, and the surface pressure,

is given by the following equation:

where

is equal to the surface tension of the water and

is the surface tension due to the monolayer. But the concentration-dependence of surface tension (similar to Langmuir isotherm) is as follows:

The last equation indicates a relationship similar to ideal gas law. However, it should be noted that the concentration-dependence of surface tension is valid only when the solutions are dilute and concentrations are low. Hence, at very low concentrations of the surfactant, the molecules behave like ideal gas molecules.

Experimentally, the surface pressure is usually measured using the Wilhelmy plate. A pressure sensor/electrobalance arrangement detects the pressure exerted by the monolayer. Also monitored is the area to the side of the barrier which the monolayer resides.

A simple force balance on the plate leads to the following equation for the surface pressure:

only when

. Here,

and

are the dimensions of the plate, and

is the difference in forces. The Wilhelmy plate measurements give pressure – area isotherms that show phase transition-like behaviour of the LM films, as mentioned before (see figure below). In the gaseous phase, there is minimal pressure increase for a decrease in area. This continues until the first transition occurs and there is a proportional increase in pressure with decreasing area. Moving into the solid region is accompanied by another sharp transition to a more severe area dependent pressure. This trend continues up to a point where the molecules are relatively close packed and have very little room to move. Applying an increasing pressure at this point causes the monolayer to become unstable and destroy the monolayer forming polylayer structures towards the air phase. The surface pressure during the monolayer collapse may remain approximately constant (in a process near the equilibrium) or may decay abruptly (out of equilibrium - when the surface pressure was over-increased because lateral compression was too fast for monomolecular rearrangements).

Applications

Many possible applications have been suggested over years for LM and LB films. Their characteristics are extremely thin films and high degree of structural order. These films have different optical, electrical and biological properties which are composed of some specific organic compounds. Organic compounds usually have more positive responses than inorganic materials for outside factors (pressure, temperature or gas change). LM films can be used also as models for half a cellular membrane.

See also

References

1. ^{{Cite web|url=http://www.biolinscientific.com/zafepress.php?url=%2Fpdf%2FKSV%20NIMA%2FApplication%20Overviews%2Ffabricating-highly-organized-nanoparticle-thin-films.pdf|title=Fabricating Highly Organized Nanoparticle Thin Films|last=|first=|date=|website=Biolin Scientific|archive-url=|archive-date=|dead-url=|access-date=}}
2. ^{{cite report|author-last=Franklin|author-first=Benjamin|author-link=Benjamin Franklin|title=From Benjamin Franklin to William Brownrigg|date=7 November 1773|quote=At length being at Clapham, where there is, on the Common, a large Pond, which I observed to be one Day very rough with the Wind, I fetched out a Cruet of Oil, and dropt a little of it on the Water.6 I saw it spread itself with surprising swiftness upon the surface, but the effect of smoothing the waves was not produced; for I had applied it first on the Leeward Side of the Pond where the Waves were largest, and the Wind drove my Oil back upon the Shore. I then went to the Windward Side, where they began to form; and there the Oil tho’ not more than a Tea Spoonful produced an instant Calm, over a Space several yards square, which spread amazingly, and extended itself gradually till it reached the Lee Side, making all that Quarter of the Pond, perhaps half an Acre, as smooth as a Looking Glass.|url=https://founders.archives.gov/documents/Franklin/01-20-02-0250}}
3. ^{{Cite journal|last=Kotov|first=N. A.|last2=Meldrum|first2=F. C.|last3=Wu|first3=C.|last4=Fendler|first4=J. H.|date=1994-03-01|title=Monoparticulate Layer and Langmuir-Blodgett-Type Multiparticulate Layers of Size-Quantized Cadmium Sulfide Clusters: A Colloid-Chemical Approach to Superlattice Construction|journal=The Journal of Physical Chemistry|volume=98|issue=11|pages=2735–2738|doi=10.1021/j100062a006|issn=0022-3654}}
4. ^{{cite journal|doi=10.1021/ar600019r|title=Langmuir–Blodgett Patterning: A Bottom–Up Way to Build Mesostructures over Large Areas|date=2007|last1=Chen|first1=Xiaodong|last2=Lenhert|first2=Steven|last3=Hirtz|first3=Michael|last4=Lu|first4=Nan|last5=Fuchs|first5=Harald|last6=Chi|first6=Lifeng|journal=Accounts of Chemical Research|volume=40|issue=6|pages=393–401|pmid=17441679}}
5. ^{{cite journal|doi=10.1021/ja045713m|title=Confinement of Transmembrane Cell Receptors in Tunable Stripe Micropatterns|date=2005|last1=Purrucker|first1=Oliver|last2=Förtig|first2=Anton|last3=Lüdtke|first3=Karin|last4=Jordan|first4=Rainer|last5=Tanaka|first5=Motomu|journal=Journal of the American Chemical Society|volume=127|issue=4|pages=1258–64|pmid=15669865}}
6. ^{{Cite journal | doi = 10.1038/srep34095 | title = Large Area Fabrication of Semiconducting Phosphorene by Langmuir-Blodgett Assembly| journal = Sci. Rep.| volume = 6| pages = 34095| year = 2016| last1 = Ritu | first1 = Harneet | pmid=27671093 | pmc=5037434| arxiv = 1605.00875| bibcode = 2016NatSR...634095K}}