| 词条 | 2219 aluminium alloy |
| 释义 |
| name = A2219 | image = | image_size = | alt = | caption = | type = | density = 2.84 g/cm3[1] | abbe_number = | refractive_index = | flammability = | limiting_oxygen_index = | water_absorption_eq = | water_absorption_24h = | radiation_resistance = | uv_resistance = | youngs_modulus = {{cvt|73.8|GPa|ksi}} | tensile_strength = {{cvt|172-476|MPa|ksi}} | elongation = 3-14% | compressive_strength = | poissons_ratio = 0.33 | hardness_rockwell = | izod_impact_strength = | notch_test = | abrasive_resistance_note = | abrasive_resistance = | coeff_friction = | speed_of_sound = | melting_point = {{cvt|543|C|F}} | glass_transition = | heat_deflection_temp_note = | heat_deflection_temp = | vicat_note = | vicat = | vicat_a = | vicat_b = | upper_working_temp = | lower_working_temp = | heat_transfer_coeff = | thermal_conductivity_note = | thermal_conductivity = 116-170 W/m*K | thermal_diffusivity_note = | thermal_diffusivity = | linear_expansion = 2.25*10−5 K−1 | specific_heat = 864 J/kg*K | dielectric_constant_note = | dielectric_constant = | permittivity = | relative_permeability_note = | relative_permeability = | permeability_note = | permeability = | dielectric strength = | dissipation_factor_note = | dissipation_factor = | surface_resistivity = | volume_resistivity = 39-62 nOhm*m | chem_res_acid_c = | chem_res_acid_d = | chem_res_alcohol = | chem_res_alkali = | chem_res_aromatic = | chem_res_grease_oil = | chem_res_haloalkane = | chem_res_halogen = | chem_res_ketone = | gas_perm_temp = 20 °C | gas_perm_N = | gas_perm_O = | gas_perm_CO2 = | gas_perm_H2O = | price = | footnotes = }} 2219 aluminium alloy is an alloy in the wrought aluminium-copper family (2000 or 2xxx series). It can be heat-treated to produce tempers with higher strength but lower ductility. The aluminium-copper alloys have high strength, but are generally less corrosion resistant and harder to weld than other types of aluminium alloys. To compensate for the lower corrosion resistance, 2219 aluminium can be clad in a commercially pure alloy such as 1050 or painted. This alloy is commonly formed by both extrusion and forging, but is not used in casting.[2] The 2219 aluminium alloy in particular has high fracture toughness, is weldable and resistant to stress corrosion cracking, therefore it is widely used in supersonic aircraft skin and structural members. The Space Shuttle Standard Weight Tank was also fabricated from the 2219 alloy. Alternate designations include AlCu6Mn and A92219. It is described in the following standards:[3]
Chemical CompositionThe alloy composition of 2219 aluminium is:[3]
References1. ^[https://materialsdata.nist.gov/dspace/xmlui/bitstream/handle/11115/179/Properties%20of%20Wrought%20Aluminum.pdf?sequence=3&isAllowed=y ASM Handbook, Volume 2: Properties and Selection: Nonferrous Alloys and Special-Purpose Materials ASM Handbook Committee, p 79 DOI: 10.1361/asmhba0001060] {{Aluminium alloys}}2. ^Marks' Standard Handbook for Mechanical Engineers, 8th Ed., McGraw Hill, pp. 6-50 to 6-57 3. ^1 2219 (A92219, AlCu6Mn) Aluminum. Retrieved on 2014-12-03. 1 : Aluminium alloys |
| 随便看 |
|
开放百科全书收录14589846条英语、德语、日语等多语种百科知识，基本涵盖了大多数领域的百科知识，是一部内容自由、开放的电子版国际百科全书。