1. Discovery

2. Properties

3. Wires and tapes

4. Applications

5. References

6. External links

Bismuth strontium calcium copper oxide, or BSCCO (pronounced "bisko"), is a family of high-temperature superconductors having the generalized chemical formula Bi₂Sr₂Ca_n−1Cu_nO_2n+4+x, with n = 2 being the most commonly studied compound (though n = 1 and n = 3 have also received significant attention). Discovered as a general class in 1988,^[1] BSCCO was the first high-temperature superconductor which did not contain a rare-earth element. It is a cuprate superconductor, an important category of high-temperature superconductors sharing a two-dimensional layered (perovskite) structure (see figure at right) with superconductivity taking place in a copper-oxide plane. BSCCO and YBCO are the most studied cuprate superconductors.

Specific types of BSCCO are usually referred to using the sequence of the numbers of the metallic ions. Thus Bi-2201 is the n = 1 compound (Bi₂Sr₂CuO_6+x), Bi-2212 is the n = 2 compound (Bi₂Sr₂CaCu₂O_8+x), and Bi-2223 is the n = 3 compound (Bi₂Sr₂Ca₂Cu₃O_10+x).

The BSCCO family is analogous to a thallium family of high-temperature superconductors referred to as TBCCO and having the general formula Tl₂Ba₂Ca_n−1Cu_nO_2n+4+x, and a mercury family HBCCO of formula HgBa₂Ca_n−1Cu_nO_2n+2+x. There are a number of other variants of these superconducting families. In general, their critical temperature at which they become superconducting rises for the first few members and then falls. Thus Bi-2201 has T_c ≈ 33 K, Bi-2212 has T_c ≈ 96 K, Bi-2223 has T_c ≈ 108 K, and Bi-2234 has T_c ≈ 104 K. This last member is very difficult to synthesize.

Discovery

BSCCO as a new class of superconductor was discovered around 1988 by Hiroshi Maeda and colleagues^[1] at the National Research Institute for Metals in Japan, though at the time they were unable to determine its precise composition and structure. Almost immediately several groups, and most notably Subramanian^[2] et al. at Dupont and Cava^[3] et al. at AT&T Bell Labs, identified Bi-2212. The n = 3 member proved quite elusive and was not identified until a month or so later by Tallon^[4] et al. in a government research lab in New Zealand. There have been only minor improvements to these materials since. A key early development was to replace about 15% of the Bi by Pb, which greatly accelerated the formation and quality of Bi-2223.

Properties

BSCCO needs to be hole-doped by an excess of oxygen atoms (x in the formula) in order to superconduct. As in all high-temperature superconductors (HTS) T_c is sensitive to the exact doping level: the maximal T_c for Bi-2212 (as for most HTS) is achieved with an excess of about 0.16 holes per Cu atom.^[5][6] This is referred to as optimal doping. Samples with lower doping (and hence lower T_c) are generally referred to as underdoped, while those with excess doping (also lower T_c) are overdoped. By changing the oxygen content, T_c can thus be altered at will. By many measures, overdoped HTS are strong superconductors, even if their T_c is less than optimal, but underdoped HTS become extremely weak. The application of external pressure generally raises T_c in underdoped samples to values that well exceed the maximum at ambient pressure. This is not fully understood, though a secondary effect is that pressure increases the doping. Bi-2223 is complicated in that it has three distinct copper-oxygen planes. The two outer copper-oxygen layers are typically close to optimal doping, while the remaining inner layer is markedly underdoped. Thus the application of pressure in Bi-2223 results in T_c rising to a maximum of about 123 K due to optimization of the two outer planes. Following an extended decline, T_c then rises again towards 140 K due to optimization of the inner plane. A key challenge therefore is to determine how to optimize all copper-oxygen layers simultaneously. Considerable improvements in superconducting properties could yet be achieved using such strategies.

BSCCO is a Type-II superconductor. The upper critical field H_c2 in Bi-2212 polycrystalline samples at 4.2 K has been measured as 200 ± 25 T (cf 168 ± 26 T for YBCO polycrystalline samples).^[7] In practice, HTS are limited by the irreversibility field H*, above which magnetic vortices melt or decouple. Even though BSCCO has a higher upper critical field than YBCO it has a much lower H* (typically smaller by a factor of 100)^[8] thus limiting its use for making high-field magnets. It is for this reason that conductors of YBCO are preferred to BSCCO, though they are much more difficult to fabricate.

Wires and tapes

BSCCO was the first HTS material to be used for making practical superconducting wires. All HTS have an extremely short coherence length, of the order of 1.6 nm. This means that the grains in a polycrystalline wire must be in extremely good contact – they must be atomically smooth. Further, because the superconductivity resides substantially only in the copper-oxygen planes, the grains must be crystallographically aligned. BSCCO is therefore a good candidate because its grains can be aligned either by melt processing or by mechanical deformation. The double bismuth-oxide layer is only weakly bonded by van der Waals forces. So like graphite or mica, deformation causes slip on these BiO planes, and grains tend to deform into aligned plates. Further, because BSCCO has n = 1, 2 and 3 members, these naturally tend to accommodate low angle grain boundaries, so that indeed they remain atomically smooth. Thus first-generation HTS wires (referred to as 1G) have been manufactured for many years now by companies such as American Superconductor Corporation (AMSC) in the USA and Sumitomo in Japan, though AMSC has now abandoned BSCCO wire in favour of 2G wire based on YBCO.

Typically, precursor powders are packed into a silver tube, which is then extruded down in diameter. These are then repacked as multiple tubes in a silver tube and again extruded down in diameter, then drawn down further in size and rolled into a flat tape. The last step ensures grain alignment. The tapes are then reacted at high temperature to form dense, crystallographically aligned Bi-2223 multifilamentary conducting tape suitable for winding cables or coils for transformers, magnets, motors and generators.^[9][10] Typical tapes of 4 mm width and 0.2 mm thickness support a current of 200 A at 77 K, giving a critical current density in the Bi-2223 filaments of 5×10⁵ A/cm². This rises markedly with decreasing temperature so that many applications are implemented at 30–35 K, even though T_c is 108 K.

For making superconducting chips, it was suggested that due to advances in blue laser technology notably 445, 450 and 405nm single mode diodes it may be possible to selectively nudge the Sr atoms in Bi-2223 to preferentially form high-Tc materials designed for computer chips. If so then the setup for making these in bulk may be very simple such as a Mott insulator pellet surface modified with BSCCO via MOVCD and then laser annealed under oxygen at a very specific set of electrostatic fields, temperatures and wavelengths sequentially, with the polarization aligned to the grain boundaries. If the 2223 variant is used then Tc may substantially increase and thus make the material suitable for a quantum sensor, SQUID and other applications needing these parameters. This idea was suggested on Twitter and a paper is being compiled with further information for release around 3Q 2018 and further discussions on 4HV.org.

The original idea was inspired by the single glowing strontium atom sitting between electrostatic plates in a vacuum which incidentally won the PhD student responsible an award.^[11]

Applications

• 1G conductors made from Bi-2223 multifilamentary tapes.
• Testing BSCCO tapes at CERN

References

External links

• BSCCO-2223 tape at US Lab
• Research fabrication of 2212 on MgO in 1993 (pdf)
• Local Electronic Structure of Bi2Sr2CaCu2O8 near Oxygen Dopants ...
• [https://arxiv.org/abs/cond-mat/0507106v1 The change of Fermi surface topology in BiSrCaCuO-2212 with doping.]

• Frank Marshall (rugby referee)
• Frank Marshall (umpire)
• Frank Marsh (disambiguation)
• Frank Marsh (Nebraska)
• Frank Martin (Australian footballer)
• Frank Martinez
• Frank Martinez (artist)
• Frank Martin (sculptor)
• Frank Martin (sport administrator)
• Frank Martin (Transporter)
• Frank Martin Williams
• Frank Martínez
• Frank Martínez (artist)
• Frank Mason (American football)
• Frank Mason III
• Frank Massa
• Frank massar
• Frank Massar
• Frank masser
• Frank Mather (footballer)
• Frank Mathews (disambiguation)
• Frank Matterson
• Frank Matthews
• Frank Matthews (disambiguation)
• Frank Matthews Leslie